COMPARATIVE EVALUATION OF SEALING ABILITY OF MINERAL TRIOXIDE AGGREGATE, RESIN MODIFIED GLASS IONOMER CEMENT AND CALCIUM PHOSPHATE CEMENT IN FURCATION PERFORATION REPAIR: AN IN-VITRO STUDY
Dr. Archana B. Satpute, Dr. Ankit V. Patel
Abstract :
A perforation is an undesirable communication between the root canal system and the supporting tissues or both. In endodontics, root perforations are referred as the second greatest cause of treatment failure next to improper obturation. Many materials and techniques have been tried to repair the furcation perforation. The purpose of this study was to evaluate the sealing ability of mineral trioxide aggregate,resin modified glass ionomer cement and calcium phosphate cement to repair the furcation perforation. The results of the studydemonstrated that the microleakage was least when perforation was repaired with mineral trioxide aggregateand it was maximum when perforation was repaired with calcium phosphate cement.
Keywords :
Furcation Perforation Mineral Trioxide Aggregate Resin Modified Glass Ionomer Cement Calcium Phosphate Cement Sealing Ability
Article:
Download PDF
DOI : 10.36106/ijsr
Cite This Article:
Dr. Archana B. Satpute, Dr. Ankit V. Patel, COMPARATIVE EVALUATION OF SEALING ABILITY OF MINERAL TRIOXIDE AGGREGATE, RESIN MODIFIED GLASS IONOMER CEMENT AND CALCIUM PHOSPHATE CEMENT IN FURCATION PERFORATION REPAIR: AN IN–VITRO STUDY, INTERNATIONAL JOURNAL OF SCIENTIFIC RESEARCH : Volume-7 | Issue-8 | August-2018
Number of Downloads : 196
References :
Dr. Archana B. Satpute, Dr. Ankit V. Patel, COMPARATIVE EVALUATION OF SEALING ABILITY OF MINERAL TRIOXIDE AGGREGATE, RESIN MODIFIED GLASS IONOMER CEMENT AND CALCIUM PHOSPHATE CEMENT IN FURCATION PERFORATION REPAIR: AN IN–VITRO STUDY, INTERNATIONAL JOURNAL OF SCIENTIFIC RESEARCH : Volume-7 | Issue-8 | August-2018
Our Other Journals...
-
Indian Journal of
Applied Research Visit Website -
PARIPEX Indian Journal
of Research Visit Website -
Global Journal for
Research Analysis Visit Website